YEOLCOAT
Yeolcoat QT606 is A pure silicone resin based heat resistant paint containing inorganic pigments. After curing,
very good resistant to thermal shock conditions from ambient temperature to 600 ℃/1112 ℉, and provides exc preventing property. Also, it has outstanding electric insulation and resistance to weathering. Recommended use
As a heat resistant paint for use on stove, motor, boiler, heater, ship' s engine, muffler, ventilator, steam lines and similar thermal implements operating from ambient temperature to 600 ℃/1112 ℉.
Physical properties Finish and color
Film thickness
20 ~ 25 ㎛ dry.
Flat. Sliver 9180, Black 1999, Grey
Drying time
Set to touch Dry to hard
May be specified in anoth
5℃/4 5℃/41℉ 1℉
20℃/ 20℃/68 68℉ ℉
30℃/ 30℃/86 86℉ ℉
4hours 24hours
1hours 10hours
30min 8hours
than indicated depending on area of use. Recoating Interval
At 20 ℃/ 68 ℉, Min. : 1 h, M
For full hardness, the coating should be exposed
Shelf Life
12 months
in service at temperature of 200℃/392℉ over
Heat Resistance
Continuous : 600 ℃/1112 ℉
1 hour time period Solids by volume
(Non-immersion service)
Silver : approx. 36%, Black : approx. 26% Grey : approx. 40%
Silver : 18㎡/ℓ, Black : 13㎡/ℓ, Grey : 20㎡/ℓ
(Theoretical)
in 20um dryfilm thickness on a smooth surface.
Specific gravity
1.21 ~ 1.75 (㎏/ℓ) according (㎏/ℓ) according to color.
Flash point
26 ℃/79 ℉ (Closed cup)
Application details
Preceding coat
4L / 18L
(Determined by ISO 3233)
Spreading rate
Surface preparation
Packing
*The packing should be turne
a month to prevent the depo Chemical Resistance
Acid Acidss Spla Splash sh & Spil Spillage l age Fair Fair Fumes Fair
Alka Alkalilis Sol Poor Poor Fair
Remarks Abrasive blasting to Sa 2½ “Near White Metal”.
1. Avoid prolonged breathing of solvent vapors.
Remove any rust, dust, grease, oil and other
2. Use with adequate ventilation.
cont contam amin inan ants ts from from surf surfac ace e to to be be coa coate ted. d.
3. Resp Respir irat ator oryy pro prote tect ctio ion n is is rec recom omme mend nded ed when when ap
Can be applied directly to the well cleaned surface.
in confined spaces or stagnant air.ventilation.
But, for for better better anti-corrosive anti-corrosive effect, effect, Yeolcoat Yeolcoat Primer Primer
4. Keep Keep away from from sparks sparks and open open flams. flams.
QP160 or suitable suitable preceding preceding coat coat may be applied applied
5. Although Although this product dry rapidly rapidly in in air, it remains remains
as a primer by specification.
Application conditionssemester The surface should be completely cleaned and dried. Master your with Scribd Do not apply apply when when relative relative humidity humidity is above above 85%. 85%. & The New York Times The surface temperature should be at l east 2.7 ℃ (5℉)$4.99/month. above dew point to prevent condensation. In Special offer for students: Only confined areas, ventilate with clean air during
until exposed to heat over 200℃/392℉, and may be mechanical damage.
Foron Days Sign to vote titlete-term 6. However, HoweRead ver, itup isFree unaffecte una ffected d30 bythis moderate-ter modera m weath
Useful Not 7. Unduly coats result in useful impaired adhesion. heavy Cancel anytime.
8. Keep the recommended dry film thickness.
Home
Saved
Top Charts
Books
Audiobooks
Magazines
News
Documents
Sheet Music
Master your semester with Scribd & The New York Times Special offer for students: Only $4.99/month.
Upload
Sign In
Read Free For 30 Days Cancel anytime.
Join